Novel composite meshes to evaluate their structural property and in vivo biocompatibility for tissue repair

Abstract

Composite meshes of different types have been prepared and used for tissue repair in pelvic floor disorder. An interlocking texture mesh (inter-mesh) and a membrane coated mesh (electro-mesh) have been used based on their structural property and biocompatibility. The proportion of degradation material in inter-mesh (69.6%) is found extremely higher than that of electro-mesh (3.22%), thus leading to higher product weight (65.50±2.31 g/m²) and thickness (0.500±0.025 mm). After 4 weeks of implantation in animal experiment, inter-mesh with surrounding tissues is observed to have higher breaking strength in tensile behavoir and better flexibility. Tissues on inter-mesh are found to grow faster with larger thickness (0.76±0.033 mm). The surface area loss of inter-mesh (2.49±0.25%) is much less than that of electro-mesh (7.49±0.63 %) within the first 2 weeks of implantation. However, the material’s degradation is accelerated after 2 weeks, leading to a higher shrinkage of 13.12±1.48 %.